Calcium Aluminate Cement, Sare Aluminate Cement A600, A700.G9, CA-70, CA-80

Sharaxaad Gaaban

Porosity hoose, xasilloonida kiimikada sare, waxqabadka heerkulka sare, caabbinta xirashada sare

HADDA LA XIRIIR

Astaamaha

Porosity hoose, xasilloonida kiimikada sare, waxqabadka heerkulka sare, caabbinta xirashada sare

Faahfaahinta xogta

Alaabta waxaa sida caadiga ah loo isticmaalaa sida alaabta foornada kala duwan ee biraha, petrochemical, batroolka, mishiinada, qalabka dhismaha iyo warshadaha kale.

Sibidhka Alumina Sare ee CA-50

Walxaha			Unug	A600	A700	G9
Halabuurka kiimikada	Al₂O₃		%	50-60	50-60	53.5 ugu badnaan
	CaO		%	33 daqiiqo	33.00 daqiiqo	33.00 daqiiqo
	SiO₂		%	8.00max	8.00max	5.50 max
	Fe₂O₃		%	2.50 max	2.50 max	2.50 max
	RO₂		%	0.4max	0.40 max	0.40 max
Dusha Gaarka ah ee Aea			cm³/g	3000max	3000max	350min
Dejinta bilowga			min	60min	60min	90min
Dejinta Dhamaadka			h	6max	6max	6 daq
Xoog Laabashada		1 maalin	Mpa	5.50 max	7.00 daqiiqo	8.00 daqiiqo
Xoog Laabashada		3 maalin	Mpa	6.50max	8.00 daqiiqo	10.00 daqiiqo
Xoog isku dhejisan		1 maalin	Mpa	40.00max	50.00 daqiiqo	72.00 daqiiqo
Xoog isku dhejisan		3 maalin	Mpa	50.00max	60.00 daqiiqo	82.00 daqiiqo
Refractories			℃	1350	1350	1450

Calcium Alumina Cement

Walxaha			Unug	CA-70	CA-80
Halabuurka kiimikada	Al₂O₃		%	68.50-72.00	78.50-81.00
	CaO		%	28.0-31.50	17.00-20.00
	SiO₂		%	≤0.50	≤0.40
	Fe₂O₃		%	≤0.50	≤0.30
	K₂O+Na₂O		%	≤0.50
Dusha Gaarka ah ee Aea			Cm²/g	≥5000	≥7000
Dejinta bilowga			min	≥45	≥30
Dejinta Dhamaadka			h	≤6	≤6
Xoog Laabashada		24h	Mpa	≥7.0	≥5.50
Cadaadis Xoog		24h	Mpa	≥45	≥40
Refractories			℃	≥1600	≥1790