Magnesium aluminium spinel (MgAl2O, MgO · Al2Oor MA) waxay leedahay sifooyin heerkul sare oo heerkul sare ah, iska caabin heer sare ah iyo iska caabin daxalka.Waa dhoobada heerkulka ugu sarreeya ee caadiga ah ee nidaamka Al2O-MgO.Kobaca doorbidka ah ee calcium hexaluminate (CaAl12O19, CaO · 6AlO ama CA6) miraha crystal ee ay weheliyaan diyaaradda basaska waxay ka dhigtaa inay u koraan qaab-dhismeedka platelet ama irbada, taas oo si weyn kor ugu qaadi karta adkaanta walxaha.Calcium dialuminate (CaAlO ama CaO · 2Al203, CA2) waxay leedahay iskudhaf hoose oo balaadhinta kulaylka.Marka CAz lagu daro walxo kale oo leh barta dhalaalaysa sare iyo is-ballaadhinta sare, waxay si fiican u adkaysan kartaa waxyeelada ay keento shoogga kulaylka.Sidaa darteed, isku-dhafka MA-CA waxay heleen fiiro gaar ah sida nooc cusub oo ah walxo heerkul sare ah oo heerkul sare ah warshadaha heerkulka sare sababtoo ah sifooyinka dhamaystiran ee CA6 iyo MA.
Warqadan, MA dhoobada, MA-CA2-CA dhoobada dhoobada ah iyo MA-CA dhoobada dhoobada ayaa lagu diyaariyey heerkul sare oo adag oo adag, iyo saameynta macdanta macdanta ee sifooyinka alaabta dhoobada ah ayaa la darsay.Habka xoojinta macdanta macdanta ee waxqabadka ceramics ayaa laga wada hadlay, natiijooyinka cilmi-baarista ee soo socda ayaa la helay:
(1) Natiijooyinku waxay muujiyeen in cufnaanta bulk iyo xoogga dabacsanaanta ee alaabta dhoobada MA ay si tartiib tartiib ah kor ugu kacday kororka heerkulka qulqulaya.Ka dib markii la isku dhajiyay 1600 ee 2h waxqabadka sintering ee dhoobada MA wuxuu ahaa mid liita, oo leh cufnaanta guud ee 3. 17g/cm3 iyo xoogga dabacsanaanta qiimaha 133.31MPaKordhinta macdanta Fez03, cufnaanta ugu badan ee alaabta dhoobada MA ayaa si tartiib tartiib ah u korodhay, iyo xoogga dabacsanaanta ayaa markii hore kordhay ka dibna hoos u dhacay.Marka lacagta lagu daray 3wt.%, xoogga dabacsanaanta ayaa gaadhay ugu badnaan 209. 3MPa.
(2) Waxqabadka iyo halabuurka marxaladda MA-CA6 dhoobada waxay la xiriirtaa xajmiga qaybta CaCO iyo a-AlO alaabta ceeriin, nadiifnimada a- Al2O3, heerkulka isku-dhafka iyo waqtiga haynta.Isticmaalka cabbirka qayb yar ee CaCO iyo daahir sare a-AlzO3 sida alaabta ceeriin, ka dib markii sintering at 1600 ℃ iyo haysashada 2h, dhoobada MA-CA6 la farsameeyey waxay leedahay xoog dabacsanaan weyn.Cabbirka walxaha CaCO3 wuxuu door muhiim ah ka ciyaaraa sameynta wajiga CA iyo koritaanka iyo horumarinta miraha crystal ee MA-CA6 alaabta dhoobada.Heerkulka sare, wasakhda Si ee a-Alz0 waxay samayn doontaa weji dareere ah oo ku meel gaadh ah, kaas oo ka dhigaya qaab-dhismeedka miraha CA6 oo ka soo baxa platelet una siman yahay.
(3) Saamaynta macdanta ZnO iyo Mg (BO2) z ee sifooyinka MA-CA isku-dhafka ah iyo habka xoojinta ayaa la baaray.Waxaa la ogaaday in (Mg-Zn) AI2O4 xal adag iyo wejiga dareeraha boron-ku jira ee ay sameeyeen macdanta ZnO iyo Mg (BO2) z waxay sameeyaan cabbirka hadhuudhka MA yar iyo maadada MA korodhay.Wejiyadan cufan waxaa lagu dahaadhay qaybaha MA-Microcrystalline si ay u sameeyaan unugyo cufan oo kala firdhiyey gobolka, taas oo horseedaysa isbeddelka miraha CA6 ee miraha siman, sidaas darteed kor u qaadista cufnaanta MA-CA alaabta dhoobada iyo hagaajinta xooggeeda dabacsanaanta.
(4)Iyadoo la isticmaalayo falanqeyn saafi ah Al2Oin halkii a-AlzO, MA-CA2-CA isku-dhafka dhoobada ayaa laga soo minguuriyay agabka cayriin ee saafiga ah.Saamaynta macdanta SnO₂ iyo HBO ee sifooyinka jireed iyo farsamada, qaab-dhismeedka yar-yar iyo halabuurka wajiga ee isku-dhafka ayaa la darsay.
Natiijooyinku waxay muujinayaan in xalka adag iyo boron-ku-jirta dareeraha ku-meel-gaarka ah ee ku-meel-gaarka ah ay ka muuqdaan walxaha dhoobada ka dib marka lagu daro macdanta SnO2 iyo H2BO;siday u kala horreeyaan, waxay ka dhigaysaa CA2 inay u beddesho marxaladda CA waxayna dardargelisaa samaynta MA iyo CA6, sidaas awgeed waxay hagaajinaysaa waxqabadka sintay ee walxaha dhoobada ah.Marxaladda cufan ee ay samaysay xad-dhaafka Ca ayaa ka dhigaysa xidhiidhka u dhexeeya MA iyo CA6 miraha mid adag, taas oo hagaajinaysa sifooyinka farsamada ee alaabta dhoobada.
Waqtiga boostada: Agoosto-29-2023